CROMO 1000 is a welding rod based chrome carbide.

CROMO 1000 is applied trough the oxy acetylene welding process. This product is especially designed to wear protection of surfaces wich are exposed to wear abrasion. Its gives resistance to severe abrasion as well as hardness properties (60HRc) on the base metal.

CROMO 1000 helps to keep low repair costs since the oxy acetylene welding process increases the service life of the tool or recharged surface.

CROMO 1000 can be applied on almost every metal surface exposed to severe wear.

In the agricultural field, CROMO 1000 is used for the hardfacing welding process to wear resistance on augers, sweeps, alabamas, furrowers, point cultivators, knives, blades, and more.

In the agroindustrial sector CROMO 1000 is used for the hardfacing of metal plates wich are placed in the surfaces exposed to excessive wear.

Thank to zero iron dilution, the metal base does not lose its properties, so it can maintain the surface properties and as the add hardness and abrasion resistance. This feature is ideal to obtain the best results in hardfacing.

If you want to learn the method of application, see the product application guide.

Presentation:

CROMO 1000 7.2mm x 1000mm     Packing by 25kg.
CROMO 1000 4.0mm x 500mm       Packing by 5kg.

CARACTERISTICAS:

HARDNESS, 60HRc
Abrasion Resistance, Very Good
Impact Resistance, Good
Red Hardness, Good up to 600°c
Stress Crack Relief, Yes
Welding Alloy, Cr/Mn/Si/C/Fe
Specification, AWS A5.13:2000/A5.21:2001/din 8555
Machinability, with abrasives